(16/06/1998). Solicitante/s: ROCKWOOL INTERNATIONAL A/S. Inventor/es: JENSEN, SOREN, LUND.

PRODUCTOS QUE CONTIENEN FIBRAS VITREAS COMPUESTAS DE UNA COMPOSICION QUE CONTIENE, POR PESO EN OXIDOS, 0.5-4% AL{SUB,2} O{SUB,3}, 2-10% P{SUB,2} O{SUB,5}, 0.1-4% TIO{SUB,2} JUNTO CON SIO{SUB,2} FEO, CAO Y MGO Y OPCIONALMENTE OTROS ELEMENTOS. LOS PRODUCTOS PUEDEN TENER UN BUEN COEFICIENTE DE DISOLUCION A UN PH 7.5 Y BUENAS PROPIEDADES MECANICAS INCLUSO TRAS SU EXPOSICION A LA HUMEDAD.

(16/04/1998). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: HOLSTEIN, WOLFGANG, MAUGENDRE, STEPHANE, LOHE, PETER, SCHWAB, WOLFGANG.

UNA COMPOSICION DE FIBRA MINERAL QUE ES BIOLOGICAMENTE DEGRADABLE CARACTERIZADA POR LOS SIGUIENTES CONSTITUYENTES EN PORCENTAJE DE PESO: SIO{SUB, 2} DE 40 A 67; CAO DE 20 A 45, MGO DE 0 A 12, NA{SUB, 2}O DE 0 A 10, B{SUB, 2}O{SUB, 3} DE 0 15, NA{SUB, 2}O + B{SUB, 2}O{SUB, 3} DE 0 A 25, P{SUB, 2}O{SUB, 5} DE 0 A 5, AL{SUB, 2}O{SUB, 3} DE 0 A 3, TIO{SUB, 2}, FE{SUB, 2}O{SUB, 3}, BAO, MNO, K{SUB, 2}O DE 0 A 5.

(01/12/1997). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: DE MERINGO, ALAIN, BATTIGELLI, JEAN, FURTAK, HANS, DR..

UNA COMPOSICION DE FIBRA DE VIDRIO BIOLOGICAMENTE DEGRADABLE CARACTERIZADA POR LOS SIGUIENTES CONSTITUYENTES EN PORCENTAJES DE PESO: DE 45 A 60 SIO{SUB,2}; MENOS DE 2 AL{SUB,2}O{SUB,3}; DE 10 A 16 CAO+MGO; DE 15 A 23 NA{SUB,2}O+K{SUB,2}O; DE 10 A 18 B{SUB,2}O{SUB,3}; DE 0 A 4 P{SUB,2}O{SUB,5}; DE 0 A 1 BAO; Y DIVERSOS HASTA 0.5.

(01/12/1997). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: DE MERINGO, ALAIN, BATTIGELLI, JEAN, FURTAK, HANS, DR..

SE PRESENTA UNA COMPOSICION DE FIBRA DE CRISTAL BIOLOGICAMENTE DEGRADABLE CARACTERIZADA POR LOS SIGUIENTES CONSTITUYENTES EXPRESADOS EN TANTO POR CIENTO EN PESO:.

(01/12/1997). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: DE MERINGO, ALAIN, BATTIGELLI, JEAN, FURTAK, HANS, DR..

SE PRESENTA UNA COMPOSICION DE FIBRA DE CRISTAL BIOLOGICAMENTE DEGRADABLE CARACTERIZADA POR LOS SIGUIENTES CONSTITUYENTES EXPRESADOS EN TANTO POR CIENTO EN PESO.

(16/11/1997). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: ROUYER, ELISABETH, DE MERINGO, ALAIN, HOLSTEIN, WOLFGANG, MAUGENDRE, STEPHANE.

UNA COMPOSICION DE MINERAL-FIBRA BIOLOGICAMENTE DEGRADABLE CARACTERIZADA POR LOS SIGUIENTES CONSTITUYENTES EN PORCENTAJES DE PESO: DE 50 A 60 SIO{SUB,2}; MENOS DE 2 AL{SUB,2}O{SUB,3}; DE 10 A 16 CAO+MGO; DE 14 A 19 NA{SUB,2}O+K{SUB,2}O; DE 7 A 16 B{SUB,2}O{SUB,3}; DE 0 A 4 TIO{SUB,2}; DE 0 A 5 ZRO{SUB,2}; DE 0 A 5 ZNO; DE 0 A 4 MNO; DE 0 A 5 BAO; DE 1 A 6 TIO{SUB,2}, ZRO{SUB,2}, ZNO, MNO, BAO; DE 0 A 2 FE{SUB,2}O{SUB,3}, SRO; DE 0 A 2 F,LI{SUB,2}O; DE 0 A 4 P{SUB,2}O{SUB,3}.

(16/05/1997). Solicitante/s: OWENS-CORNING BUILDING PRODUCTS LIMITED. Inventor/es: YALE, BRIAN, MASON, ALLEN FRANK, SHORROCK, PETER, EDWARDS, NORMAN ANTHONY.

UNA COMPOSICION DE VIDRIO, QUE PUEDE SER HILADO EN FIBRAS, TIENE LOS SIGUIENTES COMPONENTES EXPRESADOS COMO POR CIENTO EN PESO: SIO2 ESTA LIBRE DE OXIDO BORICO Y, EN CONSECUENCIA, EVITA LAS DIFICULTADES DE CONTAMINACION ASOCIADAS A DICHO COMPONENTE, SIN EMBARGO, SE PUEDE USAR EN MAQUINAS DE HILAR A TEMPERATURA ALTA PARA PRODUCIR FIBRAS DURADERAS.

(16/02/1996). Solicitante/s: GRUNZWEIG + HARTMANN AG. Inventor/es: NYSSEN, PETER ROGER, DIPL.-ING., WAGNER, WOLFRAM, DR., CHRISTOPH, GEERT, DR.

EL INVENTO SE REFIERE A FIBRAS VITRIFICANTES QUE SE CARACTERIZAN POR SU GRAN REDUCCION DE CANCEROGENIDAD, POSEEN UN DIAMETRO MEDIO DE < 8(MU)M Y UNA FRACCION DE MAS DEL 10% CON UN DIAMETRO < 3(MU)M Y SE COMPONEN DE UN 55 A 70% EN PESO DE SIO2; 0 A 5% EN PESO DE B2O3; UN 0 A 3% DE AL2O3; UN 0 A 6% DE TIO2; UN 0 A 2% DE OXIDO DE HIERRO; 0 A 5% DE MGO; UN 8 A 24% EN PESO DE CAO, UN 10 A 20% DE NA2O, UN 0 A 5% DE K2O Y UN 0 A 2% DE FLUORUROS.

(01/07/1995). Solicitante/s: OWENS CORNING. Inventor/es: POTTER, RUSSELL, MARSH.

BASANDONOS EN EL DESCUBRIMIENTO QUE EL AL SUB 2 O SUB 3 RETARDA EN GRAN MEDIDA LA VELOCIDAD DE DISOLUCION DE FIBRAS DE VIDRIO AISLANTES EN UNA SOLUCION PULMONAR SINTETICA, LAS FIBRAS DE VIDRIO CON BAJO CONTENIDO EN ALUMINA HAN SIDO IDENTIFICADAS COMO QUE SE DISUELVEN SIGNIFICATIVAMENTE MAS RAPIDO EN UN LIQUIDO PULMONAR. ADEMAS, ESTAS FIBRAS DE VIDRIO SIGUEN TENIENDO UNA DURABILIDAD ADECUADA PARA FINES DE AISLAMIENTO Y TIENEN PROPIEDADES FISICAS QUE PERMITEN A LOS PROCESOS ACTUALES FABRICARLAS DE MANERA AISLADA.

(16/07/1994). Solicitante/s: ZORTECH INTERNATIONAL LIMITED. Inventor/es: JACKSON, JAMES, DAVID, JOSEPH, GLOVER, DARREN JOHN, MATTHEWS, TONY MICHAEL.

UN MATERIAL DE AISLAMIENTO TERMICO MICROPOROSO FORMADO A PARTIR DE UNA MEZCLA INTIMA DE UN MATERIAL MICROPOROSO EN PARTICULAS, DESHIDRATADO Y FILAMENTOS DE VIDRIO DE REFUERZO. EL VIDRIO QUE CONSTITUYE LOS FILAMENTOS DE VIDRIO NO CONTIENE MAS DE UN 1 POR CIENTO EN PESO DE NA2O Y PREFERENTEMENTE TIENE LA SIGUIENTE COMPOSICION: SIO2 DE UN 50 A UN 100 POR CIEN EN PESO AL2O3 HASTA UN 25 POR CIENTO EN PESO B2O3 HASTA UN 8 POR CIENTO EN PESO MGO HASTA UN 10 POR CIENTO EN PESO CAO HASTA UN 21 POR CIENTO EN PESO NA2O HASTA UN 1 POR CIENTO EN PESO K2O HASTA UN 2 POR CIENTO EN PESO FE2O3 HASTA UN 1 POR CIENTO EN PESO F2 HASTA UN 1 POR CIENTO EN PESO.

(16/07/1994). Solicitante/s: ISOVER SAINT-GOBAIN. Inventor/es: FURTAK, HANS, DR., THELOHAN, SYLVIE, TIESLER, HARTMUT, COHEN,ISABELLE.

LA PRESENTE INVENCION SE REFIERE A UNA COMPOSICION DE VIDRIO PARA FIBRAS SUSCEPTIBLES DE DEGRADARSE EN UN MEDIO FISIOLOGICO. ESTAS COMPOSICIONES DE VIDRIO VENTAJOSAS CONTIENEN LOS CONSTITUYENTES SIGUIENTES, TOMADOS EN PROPORCIONES PONDERALES; SIO2 57-70 %; AL2O3 0-5 %; CAO 5-10 %; MGO 0-5 %; NA2O + K2O 13-18 %; B2O3 2-12 %; F 0-1,5 %; P2O5 0-4 %; IMPUREZAS < 2 %.

(01/01/1994). Solicitante/s: SAINT-GOBAIN RECHERCHE. Inventor/es: MAUGENDRE, STEPHANE, DUBOIS, BERNARD.

EL INVENTO TIENE POR OBJETO UN PROCESO QUE PERMITE REGULAR EL GRADO DE OXIDO -REDUCCION DE UN VIDRIO DURANTE SU ELABORACION. SEGUN EL INVENTO, LOS VIDRIOS DESTINADOS A SER TRANSFORMADOS EN FIBRAS CONTINUAS O DISCONTINUAS CONTIENEN ALREDEDOR DE 1% EN PESO DE FE2O3, EL GRADO DE OXIDACION DEL VIDRIO ES OBTENIDO INCORPORANDO EN LA MEZCLA DE PRODUCTOS VITRIFICABLES AL MENOS DOS OXIDANTES, UNO DE ELLOS ES UN NITRATO INORGANICO, EL OTRO A ELEGIR ENTRE UN COMPUESTO OXIGENADO DEL MANGANESO EN EL CUAL EL ESTADO DE OXIDACION DEL MANGANESO ES SUPERIOR A 2, EL BICROMATO DE POTASIO Y/O EL OXIDO CERICO. EL INVENTO FAVORECE EN ESPECIAL EL RECICLAJE DE DESECHOS DE PRODUCTOS A BASE DE FIBRAS DE VIDRIO EN LA MEZCLA VITRIFICABLE.

(01/12/1991). Solicitante/s: AKZO, N.V.. Inventor/es: ROEBROEKS, GERARDUS, HUBERTUS, JOANNES, JOSEPH, VOGELESANG, LAURENS BOUDEWIJN.

EL LAMINADO PRESENTA COMPORTAMIENTO A LA HENDIDURA BRUSCA MEJORADO, DE MODO QUE ES ADECUADO PARA USAR COMO MATERIAL DE CONSTRUCCION EN AVIACION Y COSMONAUTICA. COMPRENDE UNA CAPA INTERMEDIA DE MATERIAL TERMOPLASTICO REFORZADO POR FILAMENTOS DE VIDRIO CONTINUOS QUE TIENEN UN MODULO DE ELASTICIDAD DE 80 GPA POR LO MENOS. LOS FILAMENTOS DE VIDRIO ESTAN COMPUESTOS DE 58-69 % EN PESO DE SIO2, 18-29 % EN PESO DE AL2O3 Y 7-9 % EN PESO DE MGO. PREFERIBLEMENTE TIENE UNA TENACIDAD DE 4 GPA POR LO MENOS Y UN ALARGAMIENTO EN LA ROTURA DE 4 % POR LO MENOS. EL MATERIAL TERMOPLASTICO PUEDE SER UNA RESINA AMORFA, QUE TIENE UNA TG MAYOR QUE 140 (GRADOS) C, TAL COMO, POR EJEMPLO, POLIARILATOS, POLI(ETER)SULFONAS, POLIETERIMIDAS O ETERES DE POLI-P-FENILENO, O UNA RESINA SEMI- O PARA-CRISTALINA, QUE TIENE UN PUNTO DE FUSION CRISTALINO MAYOR QUE 170 (GRADOS) C, TAL COMO SULFUROS DE POLIFENILENO, POLIETERCETONAS O POLIMEROS DE CRISTAL LIQUIDO.

(16/07/1989). Ver ilustración. Solicitante/s: DEPOSITION TECHNOLOGY, INC.

METODO PARA LA PRODUCCION CONTINUA DE FINA HOJA DE VIDRIO REVESTIDO POR PULVERIZACION CATODICA EN FORMA DE ROLLO. EL REVESTIMIENTO PUEDE CONSISTIR EN METALES, SEMICONDUCTORES, ALEACIONES METALICAS, OXIDOS METALICOS Y MEZCLAS DE LOS MISMOS. UNA O MAS CAPAS DE MATERIAL INTERCALADO NO ABRASIVO PARA EL VIDRIO ESTAN SITUADAS ENTRE LAS SUPERFICIES DE LA HOJA DE VIDRIO Y LAS SEPARAN. EL VIDRIO PUEDE TENER REBORDES. EL MATERIAL INTERCALADO SEPARA LAS SUPERFICIES, REBORDES INCLUSIVE, DEL VIDRIO.

(01/07/1987). Solicitante/s: MANVILLE CORPORATION.

METODO DE PRODUCIR FIBRA REFRACTARIA. COMPRENDE LAS OPERACIONES DE: A) COMBINAR DE 59 A 96% DE UNA ARCILLA SELECCIONADA DEL GRUPO FILOSILICATOS DIOCTAEDRICOS 1:1 DE LA COMPOSICION AL2SI2O5 (OH)4 Y DE 4 A 41% DE CIRCON; B) FUNDIR LA MEZCLA; Y C) TRANSFORMAR EN FIBRAS LA MEZCLA FUNDIDA; OBTENIENDOSE UNA COMPOSICION, EN % EN PESO: DE 44 A 52% DE SILICE, DE 26 A 42% DE ALUMINA Y DE 3 A 27% DE CIRCONIA; PRODUCIENDOSE FIBRAS CON UN DIAMETRO DE 2 A 7 MICRAS, UNA LONGITUD DE 1,3 A 25,4 CM Y UN CONTENIDO VARIABLE DE GRANALLA, GENERALMENTE COMPRENDIDO ENTRE 35 Y 45%. TIENE APLICACIONES INDUSTRIALES.

(16/05/1986). Solicitante/s: STANDARD ELECTRICA, S.A..

SISTEMA PARA TRANSMITIR Y ALMACENAR VALORES ANALOGICOS. CONSTA DE UNA SECCION DE ENTRADA QUE CONTIENE UN MULTIPLEXOR QUE SEPARA CADA PALABRA DE DATOS EN DOS O MAS GRUPOS DE BIT; UN CONVERTIDOR DIGITAL-ANALOGICO QUE ASIGNA UN VALOR ANALOGICO A CADA GRUPO DE BIT Y CONVIERTE EL FLUJO DE DATOS DIGITAL EN UNA SEÑAL DE DATOS ANALOGICA, UN CONVERTIDOR ANALOGICO-DIGITAL QUE CONVIERTE DE NUEVO LA SEÑAL ANALOGICA EN UN FLUJO DE DATOS DIGITAL; UN DEMULTIPLIXOR SEGUIDO DE UN BUFFER , Y UN CONTROLADOR QUE CONTROLA LA SECUENCIA DE OPERACIONES EN SINCRONISMO CON LA SECUENCIA DE OPERACIONES EN LA SECCION DE ENTRADA ; DE UN MEDIO DE ALMACENAJE PARA SEÑALES ANALOGICAS; Y DE UNA SECCION DE SALIDA.

(01/04/1983). Solicitante/s: ISOVER SAINT-GOBAIN.

PROCEDIMIENTO DE OBTENCION DE COMPOSICIONES DE VIDRIO PARA LA FABRICACION DE FIBRAS. SE PREPARA UNA MASA VITREA DE OXIDOS ALCALINOTERREAS CUYOS PORCENTAJES PONDERALES SON: 37-48% DE BIOXIDO DE SILICIO, 23-33% DE OXIDO DE CALCIO, 17-25% DE SESQUIOXIDO DE ALUMINIO, 0,1-7% DE OXIDO DE MAGNESIO, 0,1-3% DE SESQUIOXIDO DE HIERRO, 2-8% DE OXIDO DE SODIO, Y 0-7% DE OXIDO DE POTASIO, COMPLETANDOSE CON UNA CANTIDAD DE 3% DE IMPUREZAS. SE INTRODUCE DICHA MASA VITREA FUNDIDA EN UN CUERPO HUECO QUE GIRA A GRAN VELOCIDAD, DOTADO DE UNA PARED PERIFERICA PERFORADA POR NUMEROSOS ORIFICIOS, A TRAVES DE LOS CUALES EL VIDRIO SE PROYECTA HORIZONTALMENTE BAJO LA ACCION DE LA FUERZA CENTRIFUGA.

(16/12/1982). Solicitante/s: PILKINGTON BROTHERS LIMITED.

PROCEDIMIENTO PARA FABRICAR UN PRODUCTO CEMENTOSO REFORZADO CON FIBRAS DE VIDRIO RESISTENTES A LOS ALCALIS. COMPRENDE LAS SIGUIENTES ETAPAS: PRIMERA, SE FUNDE EN CONDICIONES NO OXIDANTES UNA COMPOSICION DE VIDRIO FORMADA POR: UN 55 A UN 75% EN PESO DE SIO , UN 11 A UN 23% EN PESO DE K O, UN 6 A UN 22% EN PESO DE ZRO , UN 0,1 A UN 1% EN PESO DE CR O, UN 0,1 A UN 7% EN PESO DE AL O , Y UN 0,5 A UN 16% EN PESO DE TIERRAS RARAS Y TIO ; SEGUNDA, SE EXTRAE EL VIDRIO FUNDIDO EN FORMA DE FILAMENTOS DE VIDRIO CONTINUOS, MEDIANTE UN PROCESO DE ESTIRADO MECANICO; TERCERA, SE TROCEAN LOS FILAMENTOS DE VIDRIO Y SE INCORPORAN A UNA LECHADA DE CEMENTO ACUOSA; Y POR ULTIMO, SE ELIMINA EL AGUA DE LA LECHADA Y SE CURA EL CEMENTO.

(16/07/1982). Solicitante/s: PILKINGTON BROTHERS LIMITED.

PROCEDIMIENTO PARA FABRICAR FIBRAS DE VIDRIO RESISTENTES A LOS ALCALIS. SE FUNDEN EN CONDICIONES NO OXIDANTES UNA COMPOSICION DE VIDRIO QUE CONTIENE EN PORCENTAJE EN PESO: 55-75 POR 100 DE SILICE, 11-23 POR 100 DE OXIDOS DE METALES ALCALINOS, TAL COMO SODIO, POTASIO Y LITIO; 6-22 POR 100 DE OXIDO DE CIRCONIO; 0,1-11 POR 100 DE OXIDO DE CROMO; 0,1-7 POR 100 DE OXIDO DE ALUMINIO Y 0,5-16 POR 100 DE OXIDOS DE TIERRAS RARAS MAS OXIDO DE TITANIO, NO SUPERANDO ESTE EL 10 POR 100. EL TOTAL DE LOS COMPONENTES CITADOS NO DEBE SUPERAR EL 88 POR 100 EN PESO DEL VIDRIO, ASEGURANDOSE CON ELLO QUE LA TOTALIDAD O UNA PROPORCION SUSTANCIAL DEL CROMO CONTENIDO EN EL VIDRIO SE HALLA EN ESTADO TRIVALENTE. SE EXTRAE EL VIDRIO FUNDIDO EN FORMA DE FILAMENTOS DE VIDRIO CONTINUOS, OBTENIDOS POR ESTIRADO MECANICO A UNA TEMPERATURA NO SUPERIOR A 1350C. SE UTILIZAN PARA REFORZAR PRODUCTOS CEMENTOSOS.

(01/04/1981). Solicitante/s: PILKINGTON BROTHERS LIMITED.

METODO PARA LA FABRICACION DE FIBRAS DE VIDRIO RESISTENTES A LOS ALCALIS. SE BASA EN AÑADIR UNA CIERTA PROPORCION DE TORIA A DIVERSAS COMPOSICIONES DE VIDRIO QUE CONTIENEN CIRCONIA. SE PREPARA UNA MASA DE MATERIALES DE FABRICACION DE VIDRIO. SE ESTIRAN LAS FIBRAS DE VIDRIO EN FILAMENTOS CONTINUOS A PARTIR DEL VIDRIO FUNDIDO. SE ENCOLAN LOS FILAMENTOS Y SE UNEN FORMANDO CABOS. ESTAS FIBRAS SE EMPLEAN PARA REFORZAR PRODUCTOS CEMENTOSOS.

(16/01/1977). Solicitante/s: DYCKERHOFF ZEMENTWERKE, A. G..

Resumen no disponible.

(16/11/1976). Solicitante/s: PILKINGTON BROTHERS LIMITED.

Resumen no disponible.

(16/02/1976). Solicitante/s: PILKINGTON BROTHERS LIMITED.

Resumen no disponible.

(16/07/1975). Solicitante/s: NATIONAL RESEARCH DEVELOPMENT CORPORATION.

Resumen no disponible.

(01/04/1965). Ver ilustración. Solicitante/s: OWENS-ILLINOIS GLASS COMPANY.

Resumen no disponible.

(01/08/1961). Solicitante/s: OWENS-CORNING FIBERGLAS CORPORATION.

Un método para producir filamentos de vidrio, que incluye las operaciones de transformar estructuras silíceas vitrificadas llevándolas al estado fundido, y atenuar la masa fundida para formar filamentos de ella, caracterizado por la mejora que comprende recubrir dichas estructuras silíceas vitrificadas antes de su transformación en estado fundido, con un metal elegido del grupo consistente en los metales del grupo I, los metales del grupo II y una mezcla de los metales del grupo I y del grupo II.

(01/07/1960). Solicitante/s: PILKINGTON BROTHERS LIMITED.

Un método para fabricar vidrio borosilicato exento de sosa, caracterizado porque la mezcla u hornada empleada contiene un borosilicato o borato metálico anhidro como único componente de la mezcla que contiene boro.